In Accordance With: NB/T47018-2011 GB/T5293-1999 F5AZ-H08A F5A2H08MnA
AWS-A5.17 F7AZ-EL12 F7A2-EM12K
Welding flux is needed while submerged arc wire welding.
There are SJ101, SJ301 and SJ501 in our warehouse.
Description:
1. JN-SJ101 is fluorine alkali type sintered flux.
2. Grain size: 2.0-0.45 mm (10-60 mesh)
3. Performance:
a. easy to deslag.
b. Sulfur removal, phosphor removal and anti-rust.
c. fine appearance of weld (even in the narrow gap of deep slope entrance).
d. weld metal: good plastic toughness, low hydrogen content diffusion and fine properties of cold,heat and crack resistance.
Usage:
1. for low carbon, low alloy and pipeline steel.
2. for thick wall structures of different high-tensile steels.
Cautions:
1.The oil contamination, moisture, iron rust and other foreign substances must be removed from the welding joint.
2. It is better to weld under direct current.
3. Welding flux must be baked under 300-350°C for more than 2 hours before usage.
Chemical Compositions:
Al2O3+MnO |
CaO+MgO |
SiO2+TiO2 |
CaF2 |
S |
P |
25~30 |
25~30 |
15~20 |
15~20 |
≤0.03 |
≤0.03 |
Notes for welding:
1. Redry the flux for 2 hours at 300-350º C prior to be used.
2. Some rust, oil, moisture and other impurities must be cleared away from the area to be welded.
Application:
With suitable welding wires(H08MnA. H08MnMoA. H10Mn2), it can welding common structural steel, boiler steel, pipeline steel, etc. The flux can be used for multiple fast welding, and can be suitable for single-sided welding, especially suitable for pressure vessel, such as oil and gas pipes, tanks and cylinders of automatic submerged arc welding.
(Mechanical Performance of the Deposited Metal):
Wires |
Standard Models |
бs(Mpa) |
бb(Mpa) |
δ5 |
Akv(J) |
HO8A |
F4A2-HO8A |
≥330 |
≥420 |
≥22% |
≥27 |
HO8MnA |
F5A2-HO8MnA |
≥400 |
≥500 |
≥22% |
≥27 |
Fit |
GB/T5293-1999 |
F4A2-H08A |
F5A2-H08MnA |
Equivalent to |
AWS-A5·17 |
F6A2-EL12 |
F7A3-EM12 |
Mechanical Property:(according to GB5293-1999 F4A1-H08A)
Test Item |
Tensile Strength
(MPa) |
Yield Strength
(MPa) |
Elongation
(%) |
Impact Absorption Rate
(J) |
-40οC |
Guaranteed Value |
410~550 |
≥330 |
≥22.0 |
≥27 |