High Cellulose Type Covered Electrodes E6011

• Type: E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
• Material: Carbon Steel
• Diameter: 3.2mm
• Length: 300-400mm
• Welding Core Type: Carbon Structural Steel
• Electrode Coating Type: High Cellulose
• Model NO.: AWS E6011
• Slag Characteristic: Alkaline
• Stainless Steel Welding Rod Type: Carbon Steel
• Function: Low Hydrogen Type Electrode, Gravity Electrode
• Welding Power: AC or DC
• Model No.: Welding Rod Aws E6011
• Size: 2.0mm-5.0mm
• Sample: Can Offered
• OEM: Acceptable
• Quality System: ISO 9001: 2008
• Transport Package: 5kgs/Box, 4 Boxes/Carton, 50ctns/Pallet
• Specification: 2.0mm, 2.4mm, 3.2mm, 4.0mm, 5.0mm
• Trademark: QILU BRAND
• Origin: Qingdao, Shandong, China
• HS Code: 8311100000
• Production Capacity: 7000mt/Year

Product Description

AWS A5.1    E6011
AWS A5.1M  E4311
EN ISO      E35 3 C 21

Description:
AWS E6011 is a high cellulose type covered welding electrodes for DC and AC welding, excellent performance in vertical down and overhead positions on root pass, suitable for the welding of heat exchange pipes, oil tanks, ships, and boilers.


Typical chemical composition of weld metal (%)

C	Mn	Si	Cr	Ni	Mo
0.142	0.48	0.38	0.014	0.018	0.004

Typical mechanical properties of weld metal 

Yield strength      (MPa)	Tensile strength     (MPa)	Elongation(%)	Impact valume J (ºC)
440	540	22	48 (-30)

Size and recommended current (AC and DC)

size (mm)	2.5x300	3.2x350	4.0x400	5.0x500
current(A)	40-80	80-110	110-150	150-180

X-Ray radiographic inspection : Grade II

Notice:
1. If the electrodes are affected with damp, they must be baked under 80ºC for 1.5 hours before welding.
2. The stains on the weldments, such as oil stains, rust, moisture etc., must be cleared away before welding.
3.The electrode weaving should not be too wide and the strength of the arc should be suitable.