Specification: EN760 SA FB1 65 AC H5
AWS A5.17/5.23 F6A0-EL8 F7A2-EM12K F7A4-EH14
Applications:
Horizontal welding of oil storage tanks, ships, bridges, pressure vessels, penstocks, boilers and structural
steels.
Characteristics:
TY-SJ101 is an agglomerated fluoride-basic type flux.
Metallurgical behavior: Slight silicon pick up. The behavior of manganese is neutral.
Basicity: 1.8 (B||W)
TY-SJ101 assures excellent weldability, and the welding bead appearance is beautiful and the slag is easy
to remove.
The diffusible hydrogen content in deposited metal is less than 5ml/100g, so it has very good toughness
at low temperature, therefore, crack resistance is extremely high.
It is suitable for submerged arc twin-wire, tandom and multi-wire welding as well as for welding with the
two-run technique.
Damp flux should be re-dried at 300-350ºC for 2 hours. Rust, grease and moisture on the weldment
should be removed before welding.
Packing Details: Welding flux SJ101 packing: Brown paper bag with anti-moisture plastice lining. 25
kgs/Bag, 40 Bags/Pallet, 1 MT per pallet.
Chemical Composition of SJ101(%)
SiO2+TiO2 |
CaF2 |
Al2O3+MnO |
CaO+MgO |
S |
P |
15-20 |
15-20 |
25-30 |
25-30 |
≤0.05 |
≤0.05 |
Mechanical Properties of the ALL-WELD
Wires matched |
Yield point
σs (MPa) |
Tensile Strength
σb(MPa) |
Elongation
δ5(%) |
Charpy V Notch Impact value AKV (J) |
-20ºC |
-40ºC |
EM12K |
≥400 |
490-600 |
≥22 |
≥50 |
|
EH14 |
≥400 |
500-650 |
≥22 |
≥50 |
≥50 |