Agglomerated Welding Flux Sj101g

• state: Solid
• pH: Alkaline
• Type: Inorganic
• Melting Point: >600℃
• Chemical Composition: MnO=15%-30%
• Function: Protect Weld Metal
• Model NO.: SJ101G
• Application: Submerged-arc Welding
• Manufacturing Method: Smelting
• Grain Size:2.0-0.45mm (10-40 Mesh): 25kg/Kraft Paper & 1000kg/Jumbo Bag
• Transport Package: 25kg/Kraft Paper Bag & 1000kg Jumbo Bag
• Specification: size: 10-40 Mesh
• Trademark: QILU BRAND
• Origin: Shangdong
• HS Code: 38109000
• Production Capacity: 20000 Mt/Year

Product Description

Agglomerated flux SJ101G
AWS F7A4-EH14
EQUIV F7A0-EA2-A2
DIN BFB165AC12MHP5

Description:
Agglomerated flux SJ101G is a kind of fluride-alkaline sintered flux, the basicity index is about 1.8. It is shaped as grey, round grains and its size is 2.0-0.45mm(10-40mesh). It can be used with either AC or DC. The wleding wire is connected to the positive elctrode when used with DC. It has stable arc combustion, good slag detachability and good appearance of weld. The weld metal has higher low-temperature impact toughness.
As a peculiar production technique is adopted, the flux possesses better moisture resistance and good strength of grains, which may satisfy the requiements for regular transportation, storage and recycling use in welding. The flux has less specific gravity when it is bulk packed. And it is consumed less in the welding.

Applications:
Match with suitable welding wires(EL12, EM12, , EH14, H08MnMoA, Ho8Mn2MoA), It can be used to weld many types of pipes, made by such as X52, X60, X70, X80 steels etc. It can also be used in multi-layer welding, double-side single-pass welding, multiple-wire welding and narrow-gap submerged arc welding.

Notes for welding:
1. Redry the flux for 2 hours at 300-350º C prior to be used.
2. Some rust, oil, moisture and other impurities must be cleared away from the area to be welded.

Composition of welding flux(%)
SiO2+TiO2	CaO+MgO	Al2O3+MnO	CaF2	S	P
18-25	28-35	25-30	18-25	≤0.06	≤0.08

 






Agglomerated flux  SJ101 Matches with the following wires equivant to the combinations for submerged arc welding:

		Chemical Compostion of Deposited Metal (%)									Mechanical Properties of Deposited Metal(Standard&Typical)
		C	Mn	Si	S	P	Cr	Ni	Mo	Cu	Yield point      ReL(MPa)	Tensile strength Rm(MPa)	Elongation A(%)	Akv   Value (J)	Application
AWS A5.17 F6A2/EL12	Standard	-	-	-	-	-	-	-	-	-	≥460	550-690	≥22	-20ºC≥27	for welding many types of pipes, made by such as X52,X60,X70,X80 steels etc.It can also be used in multi-layer welding , double-side single-pass welding, multiple-wire welding and narrow-gap submerged arc welding.
	Typical	0.06	1.42	0.32	0.004	0.018	0.024	0.057	0.275	0.151	535	590	26	126