Standard Conforming: GB/T17854-1999 F308-H0Cr21Ni10
Description:
Welding Flux HJ260 is a type of fused flux with low-manganese high-silicon medium-fluorine content, gray glassy grains in appearance. Its grain size is 2.0-0.28mm (10-60 meshes). Fused Flux HJ260 is suitable for use with DC power, filler wires connect with Positive Electrode. With low sensitivity towards below, the flux provides very good weld bead appearance.
Applications:
Used for welding of acid-proof stainless steel structures in combination with austenitic stainless steels wires such as H0Cr21Ni10, H0Cr21Ni10Ti, etc., and being applied to roll surfacing as well.
Main Constituents (%)
| SiO2 |
MnO |
CaF2 |
Al2O3 |
MgO |
CaO |
FeO |
S |
P |
| 29~34 |
2~4 |
20~25 |
19~24 |
15~18 |
4~7 |
≤1.0 |
≤0.06 |
≤0.08 |
Mechanical Properties of Deposited Metal
| Test Item |
Tensile Strength
R m (MPa) |
Elongation
A % |
|
| Guaranteed Value |
≥520 |
≥30 |
Packaging
| Unit |
bags |
Net Weight |
25Kg |
Remarks
1. Redry the flux at 300~350ºC for 2 hours before welding.
2. Impurities such as rust, greasy dirt, moisture, etc. should be cleared from welding area.